ASTM B575 Hastelloy C276 Plate Sheet Nickel Alloy Plate Custom Laser Cutting Any Size
| Product Type | Hastelloy C276 ASTM B575 Sheet, Hastelloy C276 ASTM B575 Plate |
| Specification | ASTM B575 / ASME SB575 |
| Tolerances (width / thickness) | - EN 10258/ DIN 59381)
- EN 10151 2.4819 Hastelloy C-276 Strips
- EN 10088 Hastelloy C276 SB575 strips
|
| Dimensions | - Cold rolled Alloy C276 Plates 0.5-6.4 mm
- Hot rolled Alloy C276 Plates 3.0–10.0 mm
|
| Thickness | 0.1 to 100 mm Thk |
| Width | 10-2500mm |
| Length | 2m, 2.44m, 3m, or as required |
| Finish | SATIN, 2B, 2D, BA NO (8), Cold rolled sheet (CR), Hot rolled plate (HR), No.1 finish hot rolled, 1D, No.4, BA, 8K, hairline, brush, mirror etc. |
| Hardness | Soft, Hard, Half Hard, Quarter Hard, Spring Hard |
| variety of shapes | Coils, Foils, Plates, Sheet, Strip, Plain Sheet, Checker Plates, Rolling Sheet, Flats, Clad Plates, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), Rolling Plates, Flat Shim, soft annealed, descaled, tread Plates, sheared, annealed |
ASTM B575 UNS N10276 Hastelloy C276 Sheet is widely used in a variety of sectors, which include petrochemicals, chemical oil and gas, power production, pharmaceuticals, pulp and paper processing, and wastewater treatment. Hastelloy C276 Coil has a high tolerance to matching, stress degradation, and oxidising conditions. ASME SB 575 UNS N10276 content is often resistant to salt water corrosion in crevice environments, which may trigger aggressive assault in other products which are used on a large scale. UNS N10276 plate is normally remedy heat-treated at 2050 degrees Fahrenheit and easily quenched.
The materials used to make Hastelloy C-276 UNS N10276 Cold Rolled Plate must meet not only the chemical specifications, but also the mechanical requirements which have been stated in the ASTM B575 norm. When it comes to the mechanical properties of Hastelloy c276 Plate, this alloy must meet the requisite tensile properties. Various forms such as foils, sheets, strips, clad plate, coils, and other shapes and sizes.
Melting Range Of Alloy C276 Plate
| UNS N10276 Hastelloy C276 Plate melting range |
- °F : 2415-2500
- °C: 1325-1370
|
ASTM B575 Alloy C276 Sheet, Plate & Foil Difference
- Thickness greater than 6.35 mm is called a Hastelloy C276 Plate.
- Thickness less than 0.15mm is called a Hastelloy C276 Foil.
- Thickness greater than 0.15 mm and less than 6.35mm is called a Hastelloy C276 Sheet.
Density Of Hastelloy C276 Plate
| ASTM B575 Alloy C276 Plate density |
- lb/in3 : 0.321
- g/cm3 :8.89
|
Equivalent Of Hastelloy C276 Plate
| STANDARD | WERKSTOFF NR. | UNS | JIS | GOST | EN | OR |
| Hastelloy C276 | 2.4819 | N10276 | NW 0276 | ХН65МВУ | NiMo16Cr15W | ЭП760 |
Properties Of Alloy C276 Plate
Hastelloy C276 Plate Chemical Composition
| Grade | C | Mn | Si | S | Co | Ni | Cr | Fe | Mo | P |
| C276 | 0.010 max | 1.00 max | 0.08 max | 0.03 max | 2.50 max | 50.99 min* | 14.50 – 16.50 | 4.00 – 7.00 | 15.00 – 17.00 | 0.04 max |
UNS N10276 Plate Mechanical Properties
| Element | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| Hastelloy C276 | 8.89 g/cm3 | 1370 °C (2500 °F) | Psi – 1,15,000 , MPa – 790 | Psi – 52,000 , MPa – 355 | 40 % |
| Material | Ultimate Tensile (min) | Yield Strength (Min) | Elongation % | Hardness Rb |
| Ksi | Mpa | Ksi | Mpa |
| C276 Plate | 107.4 | 741 | 50.3 | 347 | 67 | 89 |
| C276 Sheet | 115.5 | 796 | 54.6 | 376 | 60 | 86 |
C276 alloy Plate Metric Dimensions
| Plate Surface finish | Thickness (mm) | Width (max mm) |
| 2B – Cold rolled, heat treated, pickled, skin passed plate | 0.25–8.0 | 2032 |
| 2D – Cold rolled, heat treated, pickled plate | 0.4–6.35 | 1524 |
| 2E – Cold rolled, heat treated, mechanically descaled plate | 0.4–8.0 | 2032 |
| 2R – Cold rolled, bright annealed plate | 0.25–3.5 | 1524 |
| 2H – Work hardened plate | 0.4–6.35 | 1524 |
| Polished, brushed plate | 0.5–4.0 | 1524 |
Comparision Between Inconel And Hastelloy
Inconel
Inconel is a family of austenitic nickel-chromium-based superalloys.
Composition of Inconel
| Inconel | Element (% by mass) |
| Ni | Cr | Fe | Mo | Nb | Co | Mn | Cu | Al | Ti | Si | C | S | P | B |
| 600 | 72.0 | 14.0–17.0 | 6.0–10.0 | | | | 1.0 | 0.5 | | | 0.5 | 0.15 | 0.015 | | |
| 617 | 44.2–56.0 | 20.0–24.0 | 3.0 | 8.0–10.0 | | 10.0–15.0 | 0.5 | 0.5 | 0.8–1.5 | 0.6 | 0.5 | 0.15 | 0.015 | 0.015 | 0.006 |
| 601 | 58.0 | 20.0–23.0 | 5.0 | 8.0–10.0 | 3.15–4.15 | 1.0 | 0.5 | | 0.4 | 0.4 | 0.5 | 0.1 | 0.015 | 0.015 | |
| 690 | 59.5 | 30 | 9.2 | | | | 0.35 | 0.01 | 0.02 | | 0.35 | 0.019 | 0.003 | | |
| 718 | 50.0–55.0 | 17.0–21.0 | balance | 2.8–3.3 | 4.75–5.5 | 1.0 | 0.35 | 0.2–0.8 | 0.65–1.15 | 0.3 | 0.35 | 0.08 | 0.015 | 0.015 | 0.006 |
| X-750 | 70.0 | 14.0–17.0 | 5.0–9.0 | | 0.7–1.2 | 1.0 | 1.0 | 0.5 | 0.4–1.0 | 2.25–2.75 | 0.5 | 0.08 | 0.01 |
Hastelloy
Hastelloy® could be a trademark for a series of high-strength, nickel based, corrosion resistant alloys created by Haynes Worldwide.
Hastelloy Melting Point, Density and Tensile Strength
| | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| C22 | 8.69 g/cm3 | 1399 °C (2550 °F) | Psi – 1,00,000 , MPa – 690 | Psi – 45000 , MPa – 310 | 45 % |
| C276 | 8.89 g/cm33 | 1370 °C (2500 °F) | Psi – 1,15,000 , MPa – 790 | Psi – 52,000 , MPa – 355 | 40% |
| B2 | 9.2 g/cm3 | 1370 °C (2550 °F) | Psi – 1,15,000 , MPa –760 | Psi – 52,000 , MPa – 350 | 40% |
| B3 | 9.2 g/cm3 | 1370 °C (2550 °F) | Psi – 1,15,000 , MPa –760 | Psi – 52,000 , MPa – 350 | 40% |
| C4 | 8.64 g/cm3 | 1350-1400 °C | 783 | 365 | 55% |
| Hybrid BC1 | 8.83 g/cm³ | 1343 - 1443°C | 725 | 310 | 40% |
| X | 8.22 g/cm³ | 1355°C | 655 MPa | 240 MPa | 35% |
Features Of Din 2.4819 Plate
- Excellent corrosion resistance in reducing environments
- One of few materials to withstand the corrosive effects of wet chlorine gas, hypochlorite and chlorine dioxide
- Exceptional resistance to strong solutions of oxidizing salts, such as ferric and cupric chlorides
- Resistance to localized corrosion such as pitting and stress-corrosion cracking
- Low carbon content which minimizes grain-boundary carbide precipitation during welding to maintain resistance to corrosion in heat-affected zones of welded joints
- High nickel and molybdenum contents providing good corrosion resistance in reducing environments
Uses Of UNS N10276 Plate
- Equipment for processes utilizing halide or acid catalysts.
- Digesters and bleach plants in the paper industry.
- Equipment for flue-gas desulfurisation plants.
- Sulfuric acid reactors.
- Evaporators, heat exchangers, filters and mixers used in sulfuric acid environments.
- Components exposed to sour gas.
- Organic chloride process equipment.