253MA S30815 Stainless Steel Seamless Pipe ASTM EN Standard

Comprehensive Technical Report: 253MA Stainless Steel Tubing

1. Introduction and Overview

253MA (UNS S30815) is a heat-resistant austenitic stainless steel specifically engineered for applications demanding exceptional creep strength and corrosion resistance at elevated temperatures (850°C–1100°C)78. Developed in the 1980s, it achieves performance parity with high-nickel alloys through a balanced composition of chromium, silicon, nitrogen, and rare-earth cerium10. This alloy forms a protective oxide layer at temperatures up to 1150°C, enabling use in extreme non-pressure environments while offering significant cost savings over traditional alloys like 310S28.

2. Key Parameters

Chemical Composition

The strategic addition of cerium (Ce) enhances oxidation resistance, while nitrogen (N) stabilizes austenite and boosts creep strength. This composition reduces nickel content by ~40% compared to 310S alloys10.

Table 1: Chemical Composition (Weight %)

Mechanical Properties

253MA exhibits ≥20% higher strength than standard 304/310S stainless steels across all temperatures, maintaining ductility even after prolonged high-temperature exposure710.

Table 2: Mechanical Properties (Room Temperature)

3. Specifications and Standards

Product Specifications

• Dimensions:

  • Seamless Tubes: OD 5–426 mm; Wall Thickness 0.5–25 mm3

  • Welded Tubes (ERW): ½"–24" NB; (EFW): 6"–100" NB1

• Forms: Round, square, rectangular, hydraulic profiles

• Conditions: Solution-annealed at 1050°C–1150°C followed by rapid cooling7

Governing Standards

• Tube Standards: ASTM A213, A269, A358; ASME SA213, SA269, SA3581

• Material Standards: ASTM A240 (plates), A312 (pipes), A479 (bars)69

4. Equivalent Grades

253MA is standardized under multiple international designations, facilitating global procurement and compliance.

Table 3: Cross-Reference of Equivalent Grades

5. Key Advantages

• Superior High-Temperature Performance:

  • 2.5× higher creep strength at 900°C vs. 310 stainless steel8

  • Exceptional oxidation resistance up to 1150°C due to Ce-stabilized oxide layer710

• Cost Efficiency: 30% lower material cost than 310S (25Cr-20Ni) alloys10

• Microstructural Stability: Resists σ-phase embrittlement during prolonged 650°C–980°C exposure10

• Fabrication Flexibility: Excellent weldability without pre/post-heating; cold/hot formable (hot forming: 1100°C→900°C)7

6. Industrial Applications

253MA tubing excels in aggressive thermal environments:

• Energy & Process Heating: Boiler tubes, heat exchangers, superheaters (≤900°C pressure parts)510

• Combustion Systems: Burners, flame tubes, exhaust manifolds8

• Material Processing:

  • Sintering furnaces, continuous casting equipment

  • Heat treatment furnace fixtures (e.g., trays, quench racks)27

• Waste & Mineral Processing: Incinerators, cement kiln components, refractory anchors